| Material | Wood Plastic Composite | |
| Homogenous extrusion | ||
| Raw materials used | ||
| Raw materials used | PVC | approx. 46% |
| Wood dust | approx. 46% | |
| Additives | approx. 8% | |
| Material Characteristics | ||
| Density | PN-EN ISO 1183-1:2013, met A | approx. 1.35 g/cm³ ±10% |
| Coefficient of linear thermal expansion | PN-EN 1771:2000 (the rate of a temperature increase: 5 °C/min) | ≤ 3,5 x 10(-5) mC |
| Water Absorption 24h | PN-EN 317:1999/Ap:2002 | ≤ 3,5% |
| Water Absorption 7 days | PN-EN 317:1999/Ap:2002 | ≤ 7,5% |
| Swelling 24h 7 days | PN-EN 317:1999/Ap1:2002 | ≤ 1,0% ≤ 2,5% |
| Fire Resistance | EN 13501-1:2019-02 EN ISO 11925-2; EN 9239-1 |
Bfl – s2 – permitted for use in multi-story buildings, public facilities, and evacuation routes |
| Sliding friction, CEN slider, PTV dry surface moist surface | EN 13036-4:2011 | ≥ 62 ≥ 45 |
| Load bearing capacity of connectors determined by: destructive force for clip-screw, pulling out resistance | EN 408.2010 |
≥ 800 N |
| Bending Strength | EN 310:1999/Ap1: 2002 | ≥ 20 Mpa |
| Durability resistance | EN ISO 4892-2:2009+A1:2009 EN ISO 179-1:2010 MET. 1fu |
≥ 10 NkJ/m² |
| Compression Strength | EN 408:2010 | ≥ 4,0 Mpa |
| Tensile Modulus | EN 310:1999/Ap1: 2002 | |
| decking board | EN 13706-2: 2004 | ≥ 2000 Mpa |
| assembly profile – joist | ≥ 2500 Mpa | |
| Processing | ||
| Material processing | Like wood with wood processing machines: Cutting, milling, drilling, sanding, gluing and screwing | |